在濟南地區的外墻保溫與抹灰體系中，二者定位不同：抹面砂漿側重作為保溫系統最外層的抗裂防護薄層，強調與基層的高粘結、薄抹成型與平整度；抗裂砂漿多用于找平與抗裂加強層，可做得更厚，以抑制基層收縮與開裂。常見差異如下：

　　In the external wall insulation and plastering system in Jinan area, the positioning of the two is different: the plastering mortar focuses on serving as the outermost anti cracking protective layer of the insulation system, emphasizing high adhesion with the base layer, thin plastering forming and flatness; Crack resistant mortar is commonly used for leveling and crack resistant reinforcement layers, and can be made thicker to suppress base shrinkage and cracking. The common differences are as follows:

　　用途定位：抹面砂漿用于EPS/XPS/無機保溫砂漿等保溫層外的罩面與抗裂保護層；抗裂砂漿用于平整基材不平整、抗裂加強，常見于玻化微珠等無機保溫砂漿層表面或作為找平過渡層。

　　Application positioning: The plastering mortar is used as a cover and crack resistant protective layer outside the insulation layer of EPS/XPS/inorganic insulation mortar, etc; Crack resistant mortar is used to level uneven substrates and enhance crack resistance. It is commonly found on the surface of inorganic insulation mortar layers such as vitrified microbeads or as a leveling transition layer.

　　厚度與工藝：抹面砂漿多為薄層（分層抹壓、注重平整光潔）；抗裂砂漿允許更厚的抹灰厚度以發揮抗裂效果。

　　Thickness and craftsmanship: The plastering mortar is mostly a thin layer (layered plastering, emphasizing smoothness and smoothness); Crack resistant mortar allows for thicker plastering thickness to achieve crack resistance.

　　柔性/變形適應：保溫板隨環境易變形，抹面砂漿通常要求更高的柔性以降低開裂風險。

　　Flexibility/deformation adaptation: The insulation board is prone to deformation with the environment, and the plastering mortar usually requires higher flexibility to reduce the risk of cracking.

　　成本與施工：抹面砂漿因工藝與性能要求，成本通常高于抗裂砂漿。

　　Cost and construction: Due to process and performance requirements, the cost of plastering mortar is usually higher than that of crack resistant mortar.

　　質量指標側重：抹面砂漿強調粘結強度與薄層成型；抗裂砂漿除粘結外，還強調抗裂與線性收縮控制等指標。

　　Quality indicators focus on: plastering mortar emphasizes bonding strength and thin layer forming; In addition to bonding, crack resistant mortar also emphasizes indicators such as crack resistance and linear shrinkage control.

　　以上為行業通用做法與定義，濟南工程實踐亦基本按此執行

　　The above are the common practices and definitions in the industry, and Jinan engineering practice also follows them basically

　　維度抹面砂漿抗裂砂漿

　　Dimension plastering mortar crack resistant mortar

　　主要用途保溫層外的抗裂防護薄層，為后續飾面提供良好基層找平與抗裂加強層，用于基材不平整或無機保溫砂漿層表面

　　Mainly used as a crack resistant protective thin layer outside the insulation layer, providing a good base leveling and crack resistant reinforcement layer for subsequent finishing, and used for uneven substrate or inorganic insulation mortar layer surface

　　典型厚度薄層（分層抹壓，強調平整、細致）可較厚（按設計厚度抹灰以控裂）

　　Typical thickness thin layer (layered plastering, emphasizing flatness and meticulousness) can be thicker (plastering according to the design thickness to control cracking)

　　柔性/變形適應通常要求更高柔性，適應保溫板變形強調抗裂與收縮控制，適配基層收縮

　　Flexibility/deformation adaptation usually requires higher flexibility, emphasizing crack resistance and shrinkage control to adapt to insulation board deformation, and adapting to base shrinkage

　　粘結與成型與基層粘結強度高，表面平整光潔粘結要求高，表面相對略粗

　　Bonding and forming have high bonding strength with the base layer, with a smooth and polished surface and high bonding requirements. The surface is relatively rough

　　成本與施工工藝與性能要求高，成本偏高成本相對較低

　　The cost, construction technology, and performance requirements are high, with relatively high costs and low costs

　　常見體系位置EPS/XPS/無機保溫砂漿等保溫層外無機保溫砂漿層表面或找平層

　　Common system locations include EPS/XPS/inorganic insulation mortar, etc. The surface or leveling layer of the inorganic insulation mortar layer outside the insulation layer

　　指標側重粘結強度、薄層成型、抗裂防護粘結、抗裂、線性收縮控制

　　The indicators focus on bonding strength, thin layer forming, anti cracking protective bonding, anti cracking, and linear shrinkage control

　　可否替代一般不可替代；抹面更偏薄層與飾面基層一般不可替代；抗裂更偏找平與抗裂加強

　　Can it replace something that is generally irreplaceable; The thin layer of plastering is generally irreplaceable compared to the base layer of finishing; More inclined towards leveling and strengthening crack resistance

　　在濟南工程的選型建議

　　Selection suggestions for Jinan project

　　采用板類保溫系統（EPS/XPS）時，外層優先選用抹面砂漿（薄層、高粘結、高柔性，利于抗裂與后續飾面）。

　　When using board insulation systems (EPS/XPS), the outer layer should prioritize the use of plaster mortar (thin layer, high bonding, high flexibility, conducive to crack resistance and subsequent finishing).

　　采用無機保溫砂漿（如玻化微珠）時，表層或找平加強層優先選用抗裂砂漿（更厚、抗裂與收縮控制更強）。

　　When using inorganic insulation mortar (such as vitrified microbeads), crack resistant mortar (thicker, with stronger crack resistance and shrinkage control) is preferred for the surface or leveling reinforcement layer.

　　二者功能定位不同，通常不應互相替代；若僅追求經濟性而犧牲薄層成型與柔性，后期開裂與脫落風險會上升。

　　The two have different functional orientations and should not be replaced by each other; If only pursuing economy at the expense of thin layer forming and flexibility, the risk of cracking and detachment in the later stage will increase.

　　抹面砂漿多用于干燥環境、大面積暴露的罩面；抗裂砂漿多用于找平與抗裂加強的過渡位置248。

　　Mortar is commonly used for dry environments and large exposed surfaces; Crack resistant mortar is commonly used for leveling and strengthening the transition position of crack resistance.

　　常見誤區與提醒

　　Common Misconceptions and Reminders

　　認為“抗裂砂漿一定更貴/更柔”并不準確：工程上通常是抹面砂漿成本更高、柔性要求更高（因要適應保溫板變形），而抗裂砂漿可更厚、偏找平抗裂。

　　It is not accurate to believe that "crack resistant mortar must be more expensive/flexible": in engineering, the cost of plastering mortar is usually higher and the flexibility requirements are higher (due to the need to adapt to the deformation of insulation boards), while crack resistant mortar can be thicker and leveled to resist cracking.

　　將二者混用或互代：易導致開裂、空鼓、脫落或飾面不平整等質量風險，應按體系與構造層次各司其職。

　　Mixing or substituting the two can easily lead to quality risks such as cracking, hollowing, peeling, or uneven finishing, and should be handled according to the system and construction level.

　　忽視環境與厚度控制：抹面強調薄層與平整；抗裂允許更厚以控裂，但需按設計與規范執行248。

　　Neglecting environmental and thickness control: The plastering emphasizes thin and smooth layers; Crack resistance allows for thicker thickness to control cracking, but it must be carried out in accordance with the design and specifications 248.

　　施工與驗收要點簡述

　　Summary of Key Points for Construction and Acceptance

　　基層處理：清理灰塵、油污、脫模劑等，必要時潤濕基層，保證新舊界面良好結合。

　　Grassroots treatment: Clean dust, oil stains, release agents, etc., and wet the base layer if necessary to ensure good bonding between the new and old interfaces.

　　配比與攪拌：按產品技術數據嚴格控水灰比，機械或手提攪拌均勻后使用，嚴禁隨意加減料。

　　Proportioning and Mixing: Strictly control the water cement ratio according to product technical data, mix evenly by machine or hand before use, and strictly prohibit adding or subtracting materials at will.

　　分層與厚度：抹面砂漿薄層多次抹壓、收光；抗裂砂漿按設計厚度分層找平，避免一次過厚。

　　Layering and thickness: Apply a thin layer of plastering mortar multiple times for pressing and finishing; Crack resistant mortar should be leveled layer by layer according to the design thickness to avoid excessive thickness at once.

　　養護：按氣溫與產品說明適時灑水養護，防止早期失水導致開裂。

　　Maintenance: Spray water according to temperature and product instructions to prevent cracking caused by early dehydration.

　　環境與儲存：施工與儲存溫度宜≥5℃，材料防潮防雨，未用完的砂漿結塊禁用。

　　Environment and Storage: The construction and storage temperature should be ≥ 5 ℃, and the materials should be moisture-proof and rainproof. Unused mortar should not be allowed to clump together.